Bolshan, Yuri

Vegetable oils represent an ideal and renewable feedstock for the synthesis of a variety of functional materials. However, without financial incentive or unique applications motivating a switch, commercial products continue to be manufactured from petrochemical resources. Two different families of high value, functional materials synthesized from vegetable oils were studied. These materials demonstrate superior and unique performance to comparable petrochemical analogues currently on the market.

In the first approach, 3 amphiphilic thermoplastic polytriazoles with differing lipophilic segment lengths were synthesized in a polymerization process without solvents or catalysts. Investigation of monomer structure influence on the resultant functional behaviour of these polymers found distinctive odd/even behaviour reliant on the number of carbon atoms in the monomers. Higher concentrations of triazole groups, due to shorter CH2 chains in the monomeric dialkynes, resulted in more brittle polymers, displaying higher tensile strengths but reduced elongation to break characteristics. These polymers had similar properties to commercial petroleum derived thermoplastics. One polymer demonstrated self-assembled surface microstructuring, and displayed hydrophobic properties. Antimicrobial efficacy of the polymers were tested by applying concentrated bacterial solutions to the surfaces, and near complete inhibition was demonstrated after 4 hours. Scanning electron microscope images of killed bacteria showed extensive membrane damage, consistent with the observed impact of other amphiphilic compounds in literature. These polytriazoles are suited for applications in medical devices and implants, where major concerns over antibiotic resistance are prevalent.

In the second approach, a series of symmetric, saturated diester phase change materials (PCMs) were also synthesized with superior latent heat values compared to commercial petrochemical analogues. These diesters exhibit melting temperatures between 39 °C and 77 °C, with latent heats greater than 220 J/g; much greater than paraffin waxes, which are currently the industry standard. Assessment of the trends between differing monomer lengths, in terms of number of CH2 groups of the 24 diesters synthesized exhibited structure/function dependencies in latent heat values and phase change temperatures, providing an understanding of the influence of each monomer on PCM thermal properties. A synthetic procedure was developed to produce these PCMs from a low value biodiesel feedstock. Application of these PCMs in the thermoregulation of hot beverages was demonstrated using a representative diester. This PCM cooled a freshly brewed hot beverage to a desired temperature within 1 minute, compared to 18 minutes required for the control. Furthermore, the PCM kept the beverage within the desired temperature range for 235 minutes, 40 % longer than the control.

Author Keywords: Antimicrobial Surface, Click Chemistry, Green Chemistry, Phase Change Material, Polytriazole, Renewable