Rivzi, Ghaus

This thesis explores the use of 1-butene cross metathesized palm oil (PMTAG) as a feedstock for preparation of polyols which can be used to prepare rigid and flexible polyurethane foams. PMTAG is advantageous over its precursor feedstock, palm oil, for synthesizing polyols, especially for the preparation of rigid foams, because of the reduction of dangling chain effects associated with the omega unsaturated fatty acids. 1-butene cross metathesis results in shortening of the unsaturated fatty acid moieties, with approximately half of the unsaturated fatty acids assuming terminal double bonds. It was shown that the associated terminal OH groups introduced through epoxidation and hydroxylation result in rigid foams with a compressive strength approximately 2.5 times higher than that of rigid foams from palm and soybean oil polyols. Up to 1.5 times improvement in the compressive strength value of the rigid foams from the PMTAG polyol was further obtained following dry and/or solvent assisted fractionation of PMTAG in order to reduce the dangling chain effects associated with the saturated components of the PMTAG. Flexible foams with excellent recovery was achieved from the polyols of PMTAG and the high olein fraction of PMTAG indicating that these bio-derived polyurethane foams may be suitable for flexible foam applications. PMTAG polyols with controlled OH values prepared via an optimized green solvent free synthetic strategy provided flexible foams with lower compressive strength and higher recovery; i.e., better flexible foam potential compared to the PMTAG derived foams with non-controlled OH values. Overall, this study has revealed that the dangling chain issues of vegetable oils can be addressed in part using appropriate chemical and physical modification techniques such as cross metathesis and fractionation, respectively. In fact, the rigidity and the compressive strength of the polyurethane foams were in very close agreement with the percentage of terminal hydroxyl and OH value of the polyol. The results obtained from the study can be used to convert PMTAG like materials into industrially valuable materials.

Author Keywords: Compressive Strength, Cross Metathesis, Fractionation, Polyols, Polyurethane Foams, Vegetable Oils